PTFE Bronze Bushing Teflon Pipes Ptfe Tubes and Rods
Yangzhong Haiteng is expert in the extrusion of PTFE tube. We offer a very comprehensive range of standard sizes to satisfy most needs, however, we can custom extrude PTFE tube to your own size specification should you have a special requirement.
PTFE tube has many applications throughout industry. The unique properties allow the tubing to solve problems possible with no other material. Compared with similar polymers it normally has the best price/performance ratio.
Different Processes:
1.with outside diameter 1~25mm and thickness of wall 0.1~2.5mm,we choose imported polymized ptfe resin and
process it by pressing.
2.with outside diameter25~200mm and thickness of wall 1.5~8mm,we choose suspended PTFE resin and
process it by extruding.
3.with outside diameter25~1200mm and thickness of wall 5~500mm,we process it by die pressing.
|
Properties
|
Unit
|
Result
|
|
Apparent density
|
g/cm3
|
2.10-2.20
|
|
Tensile strength (min)
|
MPa
|
20
|
|
Ultimate elongation (min)
|
%
|
200
|
|
Residual Lubricant Content (max)
|
%
|
0.5
|
|
Dialectric Strength (min)
|
KV/mm
|
10
|
Features:
1)Anti-corrosion in all kinds of chemicals including nitric acid & aqua fortis.
2)Low friction,Virtually no lubrication requirement,Light weight,Resistant to corrosion and abrasion, Impact resistance,Stable chemical properties,Oil resistance,High temperature resistance,Low temperature resistance,water resistance and so on.
3)working temperature:-55~+260°C.
4)Electric insulation;good dielectric in mediums.
5)PTFE TUBE filled ptfe tube products(plastic tube pipe) Made of high-speed mixing polytetrafluoroethylene resin and certain filling resin
6)PTFE TUBE Soft and formable,Outstanding chemical properties etc.
Specifications of PTFE tube:
|
Type
|
(mm) ID
|
(mm) OD
S Type
|
(mm) OD
T Type
|
(mm) OD
L Type
|
Packing(M/R)
|
|
30
|
0.30±0.10
|
0.80±0.10
|
0.70±0.10
|
0.60±0.10
|
305
|
|
28
|
0.38±0.10
|
0.88±0.10
|
0.78±0.10
|
0.68±0.10
|
305
|
|
26
|
0.46±0.10
|
0.96±0.10
|
0.86±0.10
|
0.76±0.10
|
305
|
|
24
|
0.56±0.10
|
1.16±0.10
|
1.06±0.10
|
0.86±0.10
|
305
|
|
23
|
0.66±0.10
|
1.26±0.10
|
1.16±0.10
|
0.96±0.10
|
305
|
|
22
|
0.71±0.10
|
1.31±0.10
|
1.21±0.10
|
1.01±0.10
|
305
|
|
21
|
0.81±0.10
|
1.41±0.10
|
1.31±0.10
|
1.11±0.10
|
305
|
|
20
|
0.86±0.10
|
1.66±0.10
|
1.46±0.10
|
1.16±0.10
|
305
|
|
19
|
0.96±0.20
|
1.76±0.20
|
1.56±0.20
|
1.26±0.20
|
305
|
|
18
|
1.07±0.20
|
1.87±0.20
|
1.67±0.20
|
1.37±0.20
|
305
|
|
17
|
1.19±0.20
|
1.99±0.20
|
1.79±0.20
|
1.49±0.20
|
305
|
|
16
|
1.34±0.20
|
2.14±0.20
|
1.94±0.20
|
1.64±0.20
|
305
|
|
15
|
1.50±0.20
|
2.30±0.20
|
2.10±0.20
|
1.80±0.20
|
153
|
|
14
|
1.68±0.20
|
2.48±0.20
|
2.28±0.20
|
2.08±0.20
|
153
|
|
13
|
1.93±0.20
|
2.73±0.20
|
2.53±0.20
|
2.33±0.20
|
153
|
|
12
|
2.16±0.25
|
2.96±0.25
|
2.76±0.25
|
2.56±0.25
|
153
|
|
11
|
2.41±0.25
|
3.21±0.25
|
3.01±0.25
|
2.81±0.25
|
153
|
|
10
|
2.69±0.25
|
3.49±0.25
|
3.29±0.25
|
3.09±0.25
|
153
|
|
9
|
3.00±0.25
|
4.00±0.25
|
3.80±0.25
|
3.40±0.25
|
100
|
|
8
|
3.38±0.25
|
4.38±0.25
|
4.18±0.25
|
3.78±0.25
|
100
|
|
7
|
3.76±0.25
|
4.76±0.25
|
4.56±0.25
|
4.16±0.25
|
100
|
|
6
|
4.22±0.25
|
5.22±0.25
|
5.02±0.25
|
4.80±0.25
|
100
|
|
5
|
4.72±0.25
|
5.72±0.25
|
5.52±0.25
|
5.32±0.25
|
100
|
|
4
|
5.28±0.30
|
6.28±0.30
|
6.08±0.30
|
5.88±0.25
|
100
|
|
3
|
5.94±0.30
|
6.94±0.30
|
6.74±0.30
|
6.54±0.25
|
100
|
|
2
|
6.68±0.30
|
7.68±0.30
|
7.48±0.30
|
7.28±0.25
|
100
|
|
1
|
7.46±0.30
|
8.46±0.30
|
8.26±0.30
|
8.06±0.25
|
100
|
|
0
|
8.38±0.30
|
9.38±0.30
|
9.18±0.30
|
8.98±0.25
|
100
|
Images:
PTFE resin,filled with some filling stuff,can prolong the life of products
and strengthen the performance,eg:Graphite,Carbon ,Glass fiber ,bronze
|
Glass Fiber:
|
Increases compressive strength, rigidity and wear.
Reduces creep and cold flow
Minimal effect on chemical and electrical properties
|
|
Carbon:
|
Increases compressive strength, hardness, wear, and load properties.
Good chemical resistance
Various types and amounts of carbon can be added to alter conductivity
|
|
Graphite:
|
Reduces coefficient of friction
Reduces initial wear
Increases strength
|
|
Molybdenum Disulfide:
|
Increases hardness, stiffness, and wear
Minimal effect on chemical and electrical properties
|
|
Bronze:
|
Increases hardness and wear resistance
Increases dimensional stability and compressive strength
Not suitable for corrosive or electrical applications
|
Группа Продуктов : Продукты из PTFE > Трубка из PTFE